I am just starting out sharpening with whet stones. I have found these stones to be very nice and the instructional videos that come along with the set on knifeplanet are extremely helpful to anyone starting out. The cost of the set was very reasonable and seems to be a great value. The customer service is amazing, I lost the site for the videos and sent an email to get the information and immediately there was a reply with all of the links that I needed. I appreciate their attention to their customers!!
However, due to limited natural deposits and extensive quarrying over the centuries, true, high quality, Japanese water stones are now few and far between and are very expensive. Thus, various companies are now producing synthetic Japanese Water Stones which generally have a more consistent composition and grit size than natural stones as well as often begin somewhat harder and thus, lasting a bit longer; not to mention being cheaper to purchase.
These are unquestionably great starter stones. After all the sharpening done over the course of a couple days, they're still perfectly flat, showing little to no signs of wearing down. Mind you I did watch tons of how-to videos online before undergoing the endeavor, so I knew how to try to make the stone wear evenly. But, my 15 year old nephew who was working on the Ontario, as I told him he could have it, if he wanted to fix it up, didn't watch all those videos and I didn't see any uneven wear on his stone after working it about a half hour either.
Your task as a sharpener is to remove that fatigued metal and expose the steel underneath, the fresh strong steel and bring side A and B of the knife together at the Apex precisely, sounds easy doesn’t it? Like peeling a layer off and having a fresh start, over and over. Of course there is much more to it than this but in very basic terms, you want the abrasive properties of the water stone to abrade the fatigued metal away, like an eraser.
A sharpening stone is a stone that has got a coarse side and usually a finer side, and that is going to take and re-shape your edge and get it back down thin enough in order to sharpen it. You are basically taking something that is blunt and thinning it back down. You have to remove all of this extra metal and get it back down to where it is thin enough to cut. Very simply, all a knife is is a very thin piece of steel to split whatever you are cutting. If the knife is obviously thicker, it is like trying to cut something with a chisel; it is not going to happen.
In addition, the most prized of the natural Japanese Water Stones are quarried in the Narutaki District north of Kyoto, Japan and are commonly available as either bench stones or pocket stones in grits ranging from 120 to 12,000. On the other hand, synthetic water stones are made from Aluminum Oxide and commonly available as either bench stones or pocket stones as well in grits ranging from 220 to 8,000 and, although this is the same abrasive material used to make India Oil Stones, the difference between the two is that the binder that holds the abrasive together enables Water Stones to be much softer than India Oil Stones which, in turn, promotes faster cutting because the worn abrasive material breaks away more quickly and is replaced with fresh, sharp, abrasive material more quickly. In addition, because water stones do not become glazed or loaded with swarf like oil stones can, new abrasive particles are constantly exposed as the stone wears so it continues to cut consistently. Plus, they can be lubricated effectively with water (rather than oil which can ruin some water stones) which combines with the fine particles of abrasive from the surface of the stone to form a slurry which polishes the bevel as the stone cuts. However, it should also be noted that Water Stones do become uneven significantly faster than other types of whetstones although, their softness does make them easier to true again.
Identify the bevel angle of the blade, better known as the "rough grind angle." Every knife is at a particular angle to suit all your needs and purposes. The majority of the pocket knives have a bevel edge is 25 to 30 degrees. Call the manufacturer of the knife if you are "weary" of this. Or go online and find a specific bevel angle chart. Nevertheless, when you find the bevel, you'll see the blade is honed into it for obvious purposes. How to sharpen a pocket knife begins with learning angles.
This is a good quality stone for a beginner looking to learn about hand sharpening knives and blades. It holds up well, especially for the price point. New sharpeners are prone to gouging and scratching stones, pushing too hard, etc, and this stone handles the abuse nicely. The no slip base is very effective at cementing the stone in place, which is a critical safety feature.
I can personally verify that this will get your knives very sharp. I will spare you all the gory details, but the picture is of the instructions the ER sent me home with after stopping the bleeding and patching me up. I have to say, that’s not what I had in mind regarding “Thanksgiving tips”. So: not only will knives slide easily through spinach, but they will go through finger and fingernail like a hot knife through butter after being sharpened by this whetstone. Very clean, straight cut. Impressive, really. Just take it slow and don’t be a moron like me.
Selecting the proper coarseness for your sharpening stone is an important first step in sharpening your knife. Not every knife needs to start at the coarsest stone you have, on the other hand a very dull knife can not be sharpened on only your finest stone. Starting with the proper coarseness will ensure that you achieve the edge you need quickly. If your knife is very dull or has a nicked blade, start with your coarsest stone. The coarse stone removes material quickly so a poor edge can be refined quickly. However, the coarse stone must be followed up with your finer stone to refine the edge. If your knife is only slightly dull and just needs a quick touch up, starting at a medium or fine stone can save you time. Starting on a fine stone requires fewer steps but must only be used on an edge requiring little work.
A diamond plate is a steel plate, sometimes mounted on a plastic or resin base, coated with diamond grit, an abrasive that will grind metal. When they are mounted they are sometimes known as diamond stones. The plate may have a series of holes cut in it that capture the swarf cast off as grinding takes place, and cuts costs by reducing the amount of abrasive surface area on each plate. Diamond plates can serve many purposes including sharpening steel tools, and for maintaining the flatness of man-made waterstones, which can become grooved or hollowed in use. Truing (flattening a stone whose shape has been changed as it wears away) is widely considered essential to the sharpening process but some hand sharpening techniques utilise the high points of a non-true stone. As the only part of a diamond plate to wear away is a very thin coating of grit and adhesive, and in a good diamond plate this wear is minimal due to diamond's hardness, a diamond plate retains its flatness. Rubbing the diamond plate on a whetstone to true (flatten) the whetstone is a modern alternative to more traditional truing methods.
We tend to recommend natural Japanese water stones only to experienced users who are thoroughly familiar with the synthetic Japanese sharpening stones. Natural stones are not to everybody’s taste and there are inevitably many uncertainties with regard to their grit grade, which cannot be determined exactly, their hardness and their suitability for certain types of steel.
A: For many years there was a heated debate around this topic with manufacturer’s stating flatly the notion their products actually damaged knives was absurd, and many professional chefs claiming not only was it not absurd, it was common for mechanical sharpeners to damage expensive cutlery. So who was right? To a certain extent they both were. The manufacturers were correct in asserting that if you followed the instructions to the letter there was little if any chance your knives would be damaged. However, in reality few people actually followed the instructions to the letter and when they veered from the recommended course the potential was there for damage.
This is a great sharpener for budget conscious cooks. You can use it with equal facility whether you’re right or left handed, it has a convenient finger guard to cut down on accidents and most important, it only takes a few swipes on a regular basis to keep your knives in tip-top condition. It’s not glamorous. It won’t add anything substantive to your kitchen decor. But it will ensure your knives are always ready for whatever dish you have in mind.
For the common sharpening purpose, generally, people tend to use two phases. In the first phases, they use the coarse stone to shape the edges then jump to the finer stone. In application, these of the two phases can be extended with the grit stone in between. It might be varying in the number of grits or mesh in different types of sharpening stone.
However, because the Belgian Blue stone generally occurs in relatively wide columns with much thinner layers of Vielsalm Coticule on either side adjacent to the slate, the Belgian Blue stone is more plentiful that Coticule and thus, it’s somewhat less expensive. But, it’s also somewhat softer than Coticule and is not divided into different grades as Coticule is. Furthermore, because it is a softer stone than Coticule, it is sold without a substrate layer.